STEAM TURBINES
  • Prone to:

       -- High Cycle Fatigue (HCF)

       -- Stress Corrosion Cracking (SCC)

Chron37-12-Blades1c.jpg
00:00 / 00:57
DURING OPERATION
  • SCC 3 Occurring Conditions

       1) An alloy susceptible to stress corrosion cracking

       2) A stress intensity factor above the threshold value

       3) A corrosive environment being present

Chron37-22-Sample.jpg
00:00 / 01:38
COMPILATION & ACCURACY
  • Graphical, Photographic, Charted etc...

Chron37-14-Particle.JPG
00:00 / 00:46
Phased Array-Audio Text
  • Turbine Rotor Inspection

       -- Overview

Chron37-02-Steam Rotor Layout1.png
00:00 / 02:00
FAILURE TYPES
  • 2 Main Categories

       -- 1) Static Stresses

       -- 2) Dynamic Stresses

Chron37-11-CouplerCrack.JPG
00:00 / 01:32
PA SCREEN PRINT
  • Crack in coupler (Hole 15 to 16)

       -- Extends across 90% of the surface

       -- Extends down into material approx .800 to 1.125"

       -- Horizontal extension of .250 to .325"

Chron37-08-coupler.jpg
00:00 / 00:43
COLLECTION & REPORTING
  • Content & Context